Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)
Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)
Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)
Speed Zirconia——Speed Sintering Multilayer Zirconia Disc Open System (98mm) - CeraDirect
Speed Zirconia——Speed Sintering Multilayer Zirconia Disc Open System (98mm) - CeraDirect
Roll over image to zoom in Click on image to zoom
Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)Speed Zirconia——Speed Sintering Multilayer Zirconia Disc Open System (98mm) - CeraDirectSpeed Zirconia——Speed Sintering Multilayer Zirconia Disc Open System (98mm) - CeraDirect

Speed Multilayer Zirconia Super Speed Sintering Disc Open System (98mm)

CeraDirect

Please contact our customer service if you are unable to set up the relevant sintering curve on your machine.

Thickness: 12mm
Color: A1
Price:
$100.00 USD

Description

Ceradirect Speed Multilayer zirconia, a revolutionary product that combines the advantages of previous zirconia-based materials with the remarkable ability to achieve rapid sintering within 30 minutes. This groundbreaking feature significantly reduces the sintering time, leading to a remarkable enhancement in work efficiency.

Speed Multilayer zirconia sets a new industry benchmark and provides an efficient solution to the sintering needs of professionals.

·Suitable machines

Suitable for SpeedFire machines with 5.0 or higher systems, the curve selection is the DEMO5 demo curve.

·Super high transparency

Suitable for high aesthetic cases

·High strength

Suitable for making multi-unit restorations

·Multilayer gradient

Multi-dimensional gradient effect close to natural teeth

·Special production procedure

Excellent milling properties, accuracy of fit and edge stability

Attention

·Prepare teeth into obviously sloping shoulder or round shoulder.

·The milling thickness of edge of cervical region should be at least 1mm.

·Occlusal surface and incisal need to grind off 1.5-2.0mm.

·Knuckle radius should be 0.7mm.

·Axial surface aggregation degree should be 6-8 degree.

·For bridges, adjacent abutment teeth should be parallel between each Other to avoid undercut.

 

Shipping

DHL(default),Various other modes of transportation are available,If you want to know more shipping information, please click here

 

Ceradirect dental zirconia

Strength Transparency
 Features
HT 1400Mpa 35% Super Strength Low Transparency
SHT 1370Mpa 43% High Strength High Transparency
SHT Color 1125Mpa 43% High Transparency Preshaded Zirconia
SHTML 1100Mpa 48% 6-layers Of Color Gradients
3D-Pro Multilayer 900-1200Mpa 43%-55% 6-layers Of Color Strength Transparency Gradients
4D-Pro Multilayer 900-1200Mpa 43%-55% 6-layers Of Color Strength Transparency Gradients/Speed Sintering
Speed Multilayer 1200Mpa 45%-51% Fast Sintering In About 30 Minutes
MAX Multilayer 1000-1300Mpa 45%-57% New Technology Layerless Fusion Gradient